Title: Synthesis and Characterization of Alginate/Poly (4-vinylpyridine) Hybrid System
Authors: Yılmaz, Elvan
Alshhab, Abdallah M. H.
Eastern Mediterranean University, Faculty of Arts and Sciences, Dept. of Chemistry
Keywords: Chemistry
Polyelectrolytes
Electrolyte solutions
Sodium alginate
poly(4-vinylpyridine)
polyelectrolyte complex
multilayer
ciprofloxacin HCl
LbL
Issue Date: 2020
Publisher: Eastern Mediterranean University (EMU) - Doğu Akdeniz Üniversitesi (DAÜ)
Citation: Alshhab, Abdallah M. H.. (2020). Synthesis and Characterization of Alginate/Poly (4-vinylpyridine) Hybrid System. Thesis (Ph.D.), Eastern Mediterranean University, Institute of Graduate Studies and Research, Dept. of Chemistry, Famagusta: North Cyprus.
Abstract: Polyelectrolyte multilayer (PEC) films of sodium alginate and poly(4-vinylpyridine) were prepared by immersing the sodium alginate (Na-Alg) films into the poly(4vinylpyridine) (P4VP) in 0.1 M hydrochloric acid solution. Then, the multilayer films were formed by the alternating addition of Na-Alg and P4VP respectively. The morphology, topography and chemical structures of the PEC films and its precursors were investigated and characterized by SEM analysis, AFM and FTIR spectroscopy respectively. It was observed that the number of layers and the nature of the outer layer affect the physicochemical characteristics. The thermal properties of the PEC films were examined by thermogravimetric analysis (TGA). The onset of degradation for PEC-2, PEC-3, PEC-4 and PEC-5 is at 180°C, 195°C, 195°C and 200°C respectively. Na-Alg film, on the other hand, decomposes at 215°C while P4VP film gives its first decomposition temperature at 290°C. The crystallinity indexes were calculated by XRD analysis. Complexation reduces the crystallinity comparing with the parent membrane, Na-Alg. Crystallinity index of Na-Alg film is 0.49 whereas the values for PEC-2, PEC-3, PEC-4 and PEC-5 are 0.25, 0.36, 0.42 and 0.39 respectively. The hydrophilicity of the PEC films was examined by using contact angle measurement. When Na-Alg is the outer layer in the PEC, hydrophilicity is higher. Roughness of the film surfaces was characterized by AFM measurements. The solubility of the films was tested in different organic solvents and in aqueous solution of acidic and basic pH values. They are insoluble in water and up to pH=4.2 in acid buffer solution. The swelling properties of the PEC films were studied in acidic aqueous solution of pH value 1.2 and in water. The highest equilibrium % swelling values among the PEC films have been obtained as 215% and 155% for PEC-5, in water and acidic buffer respectively within an hour. The drug loading-release properties for the PEC were studied using ciprofloxacin HCl as a model drug. The three layer film PEC-3, which is composed of Na-Alg outer layer deposited on a P4VP/Na-Alg double layer, is characterized by the lowest roughness (Rq=16.3 nm) and the most hydrophilic surface with a contact angle value of 38.1° among all other films prepared. Its crystallinity index is 0.36, and starts to degrade at 195 °C. It exhibits 130-135% equilibrium swelling capacity in acid buffer and water respectively. PEC-3 is the film with the highest drug loading capacity and drug loading efficiency values of 3.51% and 87% respectively when the initial drug concentration is 12.5 ppm. A cumulative drug release of 65% is obtained from PEC 3 within 24 h in water when the initial concentration of the drug solution is 12.5 ppm. Several kinetic models including zero order, first order, Higuchi and Korsmeyer-Peppas were tested to understand the kinetics and mechanism of the drug release from the PEC films of Na-Alg and P4VP. The best fit was obtained with Higuchi's equation. Release mechanism was found to be Fickian according to the Korsmeyer-Peppas equation. Keywords: sodium alginate, poly(4-vinylpyridine), polyelectrolyte complex, multilayer, ciprofloxacin HCl, LbL
ÖZ:Sodyum alginat ve poli(4-vinilpiridin) den oluşan çok katmanlı polielektrolit kompleks filmler (PEK), sulu sodyum alginat (Na-Alg) ve 0.1 M HCl çözeltisinin çözgen olarak kullanıldığı asitli poli(4-vinilpiridin) (P4VP) çözeltileri ile elde edildi. Na-Alg film sırasıyla P4VP, Na-Alg çözeltilerine batırılarak çok katmanlı PEK filmler elde edildi. Na-Alg ve PEK filmlerin morfolojisi, topografisi ve kimyasal yapıları araştırılarak sırasıyla SEM, AFM ve FTIR spektroskopisi yöntemleri ile bulundu. Katman sayısının ve dış katmanın kimliğinin fizikokimyasal özellikleri etkilediği görüldü. PEK filmlerin termal özellikleri TGA yöntemi ile incelendi. Filmlerin ilk bozunma sıcaklığı PEC-2, PEC-3, PEC-4, PEC-5 için sırasıyla 180°C, 195°C, 195°C ve 200°C olarak gözlemlendi. Öte yandan Na-Alg ve P4VP filmlerin sırasıyla 215°C ve 290°C sıcaklıkta bozunduğu görüldü. Örneklerin kristallik endeksleri XRD analizi ile bulundu. Polimerler arasında kompleks oluşumunun kristallik oranını düşürdüğü gözlemlendi. Na-Alg filmin kristallik endeksi 0.49 iken bu değer PEC-2, PEC-3, PEC-4 ve PEC-5 için 0.25, 0.36, 0.42 ve 0.39 olarak hesaplandı. Filmlerin hidrofilik karakteri temas açısı ölçümleri ile bulundu. Dış katmanın Na-Alg olması durumunda hidrofilik karakterin arttığı gözlemlendi. Film yüzeyinin pürüzlülüğü AFM ölçümleri ile belirlendi. Filmlerin organik çözücülerde, suda, asidik ve bazik pH değerindeki sulu çözeltilerde çözünürlüğü test edildi; pH 4.2 değerine kadar asitli ortamda çözünmediği görüldü. Filmlerin şişme davranışları suda ve pH-1.2 asitli tampon çözeltide incelendi. PEC-5'in asitte ve suda %215 ve %155 denge şişme değerleri ile en fazla şişme değerine sahip olduğu görüldü. Filmlerin ilaç yükleme ve salım özellikleri siprofloksasin.HCl (CIP.HCl) model bileşik kullanılarak çalışıldı. Na-Alg-P4VP-Na-Alg katmanlarında oluşan üç katmanlı film, PEC-3 filmin en düşük pürüzlülük (Rq=16.3 nm) değerine sahip olduğu, ayrıca 38.1° temas açısı ile en hidrofilik yüzeye sahip olduğu belirlendi. Bu örneğin kristallik endeksi 0.36 dır ve 195°C sıcaklıkta bozunmaya başlamaktadır. Ayrıca asitli ortamda ve suda %135-130% dengede şişme değerine sahiptir. Bu özelliklere sahip PEC-3 filmin en yüksek CIP.HCl yükleme (3.51%) kapasitesi ve verimliliği (87%) değerlerini verdiği bulundu. PEC-3 filmden 24 saat sonunda suda, ilacın %65'inin salındığı hesaplandı. Salım kinetiği ve mekanizması sıfırıncı dereceden, birinci dereceden, Higuchi ve Korsmeyer-Peppas denklemlerine göre incelendi. Salım kinetiğinin Higuchi denklemine uyduğu salım mekanizmasının ise Korsmeyer-Peppas denklemine göre Fickian olduğu bulundu. Anahtar Kelimeler: sodyum alginat, poli(4-vinilpiridin), polielektrolit kompleks film, siprofloksasin HCl, LbL
Description: Doctor of Philosophy in Chemistry. Thesis (Ph.D.)--Eastern Mediterranean University, Faculty of Arts and Sciences, Dept. of Chemistry, 2020. Supervisor: Prof. Dr. Elvan Yılmaz.
URI: http://hdl.handle.net/11129/5651
Appears in Collections:Theses (Master's and Ph.D) – Chemistry

Files in This Item:

File Description SizeFormat
Alshhab Abdallah - Ph.D..pdfThesis, Doctoral3.66 MBAdobe PDFView/Open


This item is protected by original copyright

Recommend this item
View Statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback