Random copolymers of poly(ethylene glycol methacrylate) (PEGM), and diethyl
amino ethyl methacrylate (DEAEM) were synthesized at low, and high conversions
by photoinitiation. Crosslinked poly(PEGM-co-DEAEM) samples were obtained,
and characterized by FTIR, SEM, DSC, TGA, and elemental analyses. Swelling
behavior of the copolymers revealed that the copolymers acted as superabsorbent
hydrogels. The monomer reactivity ratios were calculated using Fineman Ross,
Extended Kelen Tüdøs, and Mayo Lewis methods that gave r1(PEGM)=0.90,
r2(DEAEM)=0.14 at low conversions. At high conversions r1 and r2 values were
calculated as 1.01 and 0.40, respectively. Adsorption isotherms of methyl
orange(MO) onto hydrogels were studied using Langmuir, Freundlich, and Temkin
models. The experimental data fitted well with the Langmuir equation. The
maximum adsorption capacity for MO was 212.7 mg g-1
at pH=3. The adsorption
data gave best fit with the pseudo-second order kinetic model. Thermodynamic
evaluation showed spontaneous nature for MO adsorption onto poly(PEGM-coDEAEM ) hydrogels.
Poly(2-hydroxyethyl methacrylate ) was grafted onto poly(vinyl cinnamate) by
photoinitiation using benzophenone (Ph2CO) as initiator, at 360 nm wavelength, and
at a total power of 7670 µW.cm-2
. The grafting process was optimized by changing
the concentration of HEMA, Ph2CO, chemical crosslinker ethylene glycol
dimethacrylate (EGDMA), and UV irradiation time. The polyVCi-graft-polyHEMA
films obtained were characterized by FTIR and SEM. The contact angle
measurments revealed enhancement of wettability of the polyVCi backbone via the
grafting with polyHEMA. TGA analysis confirmed thermal stablility of the films.
Swelling behaviors of films were examined in both water and ethanol. Successful
photo-encapsulation of flurbiprofen into the film matrixes was confirmed. The
PolyVCi-graft-PolyHEMA films proved to be suitable release matrixes for
flurbiprofen demonstrating pulsatile release behavior. Zero-order model fitted the
flurbiprofen release mechanism. This mechanism was ensured through its RitgerPeppas “n” value (1.00 to 1.41), which indicates super case II release kinetics.
ÖZ:
Poli(etilen glikol metakrilat) (PEGM) ve dietil amino etil metakrilat (DEAEM)
yapıtaşlarından oluşan rasgele kopolimerler UV başlatıcı ile düşük ve yüksek
verimler ile sentezlendi. Elde edilen çapraz bağlı polimerler FTIR, SEM, DSC, TGA
ve elemental analiz yöntemleri ile karakterize edildi. Sulu ortamda şişme
davranışlarının incelenmesi sonucu elde edilen kopolimer hidrojellerin
süperabsorban malzemeler oldukları belirlendi. Monomer reaktiflik oranları Fineman
Ross, Extended Kelen Tüdøs, and Mayo Lewis metodları ile düşük verimde
r1(PEGM)=0.90, r2(DEAEM)=0.14 ve yüksek verimde 1.01 and 0.40 olarak
hesaplandı. Metil oranj'ın (MO) hidrojeller üzerine adsorplanması çalışılarak
Langmuir, Freundlich, and Temkin modellerine göre incelendi. Veriler Langmuir
modeline yüksek uyum sağladı. En yüksek MO adsorplama kapasitesi pH=3'te 212.7
mg g1
olarak bulundu. Adsorpsiyon davranışının psödo ikinci dereceden kinetik
davranış gösterdiği belirlendi. Adsorpsiyon davranışının termodinamik bakımdan
spontane olduğu saptandı.
Poli(2-hidroksietil metakrilat) (poliHEMA) poli(vinil sinnamat) (poliVCi) üzerine
UV başlatıcı ile benzofenon kullanılarak aşılandı. Aşılanma davranışı HEMA,
benzofenon, çapraz bağlayıcı ve radyaysona maruz bırakılan zaman açısından
optimize edildi. Elde edilen film örnekler FTIR, SEM ve TGA yöntemleri ile
karakterize edildi. Kontak açısı ölçümleri poliVCi yüzeyinin poliHEMAile
aşılandıktan sonra daha hidrofilik bir karakter elde ettiğini gösterdi. Filmelrin hem
suda hem de etanolde şişme davranışı gösterdiği gözlemlendi. Filmlere flurbiprofen
enkapsüle edilerek flurbiprofen salım davranışınincelendi ve sıfırıncı dereceden
salım kinetiği belirlendi. Bu durum Ritger-Peppas n (1.00-1.41) değerine göre de
konfirme edildi. Aynı zamanda aralıklı salım davranışı gözlemlendi.